MECELLOSE, enviromentally friendly, uses cellulose as a primary source, which can be obtained from wood or cotton, is a water-insoluble natural polymer that has 30-65% crystallinity formed by hydrogen bonds between molecules. Through a chemical process called ‘Etherification’, this water insoluble cellulose is turned into water-soluble nonionic cellulose ether.

As thickening agent, water retention aid, binder, dispersion aid, lubricant, protective colloid or stabilizer, typical applications .Samsung fine chemicals produces MC(Methyl Cellulose),HPMC (Hydroxy Propyl Methyl Cellulose) and modified cellulose ethers that satisfy specific needs of the current and future customers.

GYPSIUM BASED PRODUCTS-MECELLOSE

* Viscosity at 20 C in % 2 solution
* * Particles size 250 micron (60mesh) under%
***Packing : 20kg
Appearence: white to very faintly off-white powder

Cellulose ethers obtained,from nature like kaolin, quartz, feldspar and clay- substances in certain mixing ratio by mixing the dough into whether then pressed ,at high temperature oven.After this process various size products have used for protection and decoration of ceramics for the building of the inner and outer surfaces,coating the floor is an important adhesive.

Prepared dry mixture of the product participate in the product prepared with water obtained mixture result in fees in the amount of water to keep providing the desired workability and provide extension of working time.

Wet adhesion and shear resistance of mortar by increasing the application provides convenience and as a result of these features of the desired ceramic floor will increase the strength of adhesion

CEMENT-BASED NORMAL CERAMIC ADHESIVE

Economic purposes are manufactured products. Cement and polymer are under the normal standart.Generally polymer not used.

Depending on request ,usage rate Mecellose is between % 0.2 to 0.3.

Products, especially high viscosity are preferred.

CEMENT-BASED STANDART CERAMIC ADHESIVE

Products produced in accordance with standard TS 11140 EN 12004 C1.

Adhesion strength is required to be at least 0.5 N/mm2

Depending on request ,usage rate Mecellose is between % 0.3 to 0.4.

TS 11140 EN 12004 C2 in accordance with standard cement and chemical additives fortified with a special high-performance products.

Adhesion strength is required to be at least 0.1 N/mm2

Depending on request ,usage rate Mecellose is between % 0.4 to 0.6.

 GYPSUM  BASED PLASTER

Obtained from nature in the raw stone plaster (gypsum-calcium sulfate dihydrate) by grinding calcined with different techniques, is produced by cooking and contributions classification. Mixed with water in the finished product will earn binding properties.

Thermal isolation, sound isolation, lightness, ease of handling and maintenance, to the surface to breathe, due to their fire-prevention features such as briquettes, bricks, gross brton, gas concrete and plaster-like surfaces are used to.

GYPSUM-BASED MACHINE PLASTER

Generally gypsum plaster machinery  be used plaster of the wall, thickness of 1-2 cm between.to application and cost minimized  the plaster machinery application is preferred. To developed the desired surface can easily discarded, the occurrence of high adhesion strength, leakage resistance and water retention property MECELLOSE will be prefered.

GYPSUM-BASED HAND PLASTER

Gypsum based plaster used in the interior of the buildings are used often. Application thickness is between 1-2 cm.

MECELLOSE is prefered in applications  because of driving convenience goods spending, high adhesion strength and water holding structure of run-time features such as extension products properties.

CEMENT-BASED JOINT FILLER MATERIALS

Such as ceramic, natural stone, glass mosaics, granite, kotto, marble, filling in gaps, coating materials used in cement based joint filler. Usually 1-6 mm in the interior, exterior will be applied in the range of 3-20 mm.

MECELLOSE products are prefered  because of spending his driving ease, cracking resistance, and within the water holding properties such as extension of working time depending on usage rate properties.

Depending on request ,usage rate Mecellose is between % 0,05 to 0.1.

CEMENT-BASED MORTARS

MECELLOSE is prefered because of Indoors and outdoors in concrete, brick, brickets, gas concrete, concrete, plaster surfaces such as bims are used to. Machine and hand application, consider, the differences are supported by various chemical additives. The desired surface of the plaster plaster applications can easily discarded, the occurrence of high adhesion strength, leakage resistance and water retention property that is developed to provide run-time features such as the extension application properties.

Depending on request ,usage rate Mecellose is between % 0.03 to 0.15

PLASTER AND CEMENT-BASED DECORATIVE COATINGS

Especially  is used in the outdoor .heat isolation plaster applied based cement surfaces, the surface smooth rough surfaces and thin plaster is applied for aesthetic purposes to provide decorative appearance. Such as easy to implement the desired surface of plaster, to create a high adhesion strength, leakage resistance and water retention property that is developed to provide run-time features the extension properties MECELLOSE is preferred.

Depending on request ,usage rate Mecellose is between % 0.1 to 0.25

CEMENT-BASED SELF-LEVELING ALUM

Interior and exterior PVC, ceramic, natural stone, marble, parquet, and carpet, coatings obtain a smooth surface before it was sticking or damaged surface of the foot and mouth are used for leveling. Increasing mortar business, shrinkage cracks may occur due to the reduction of the mortar components to prevent decomposition and water retention characteristics, such as lengthening the time of the study was developed and used because of contributions.

Depending on request ,usage rate Mecellose is between % 0.05 to 0.1